According Humaira, this is done because the plastic has been used often cause environmental pollution due to garbage piling on too long, so prone to flooding. "Plastics are usually pile up and pollute the environment for years could be degraded or decomposed by the soil only within less than a week," said the girl was born in Jombang.
Humaira explains, is a synthetic plastic food packaging materials that have a negative impact on the environment and human health. That comes from the synthesis of materials such as cellulose acetate, polyethylene, polypropylene, polyamide, polyester, polyvinyl chloride (PVC), polyvinyl acetate and aluminum foil. While plastics made from these materials are nonbiodegradable or can not be explained naturally by microorganisms in the soil.
Not only that, typically of synthetic plastics material added softener (plasticizer) that is not rigid and not easily fragile. This softener material consisted mostly of groups phthalate compounds (esters derived from phthalic acid). "In fact, the use of DEHA plasticizer such as PCBs and can cause tissue death and is carcinogenic in humans," said Humaira.
Well, this time Humaira research provides an alternative breakthrough by developing biodegradable plastics are easily degraded by microorganisms in the soil and renewable (renewable). The materials used for the manufacture of biodegradable plastics include starches aloe vera, chitosan, with glycerol as a plasticizer.
"Aloe vera contains polysaccharides that can form a layer of plastic film which has antibacterial properties. While chitosan containing proteins to strengthen the mechanical properties or strength of plastics, as well as glycerol as a plasticizer in an environmentally safe to give flexibility or elasticity in the plastic," said Humaira. That is why, plastic biodegradable from Aloe vera has advantages, which are antibacterial and easily degradable by microorganisms in the soil.
Humaira also said plastics from starch and aloe vera-chitosan prepared by chitosan concentration of three percent, four percent, five percent, six percent and seven percent (w / v). Meanwhile, aloe vera and glycerol concentration is fixed which is five percent (w / v) and 10 milliliters.
About the method, Humaira explained, the methods used in the synthesis of plastics from Aloe vera-chitosan, which is inverse phase with the solvent evaporates at a temperature of 60 degrees Celsius. "To characterize this plastic cover thickness measurement, test the mechanical properties, swelling test, determination of morphology, and the biodegradable nature of the test," he explained.
From the research, said Humaira, obtained value attractiveness percentage elongation and modulus of plastic film on the optimal composition of chitosan, starch, aloe vera and five per cent compared to seven percent (w / v), which is 461.538 MPa, respectively, 6.2 percent, and 744.416 MPa. "The percentage of swelling (swelling), the optimum was obtained at the composition of plastic between the starch-chitosan aloe five percent compared to four percent (w / v), with a value of 12.5 percent. In addition, based on Scanning Electron Microscopy results (SEM) produced morphological The flat plastic film and not hollow, "said Humaira. Thus, in a test of biodegradable plastics from Aloe vera-chitosan using EM4 bacteria showed that the degradation of plastic film in just one week
No comments:
Post a Comment